  • Ceramic Foam Filter PAL

    Ceramic Foam Filter Suppliers

    AdTech Using three-dimensional network structure and connected pores organic foam as a carrier and immerse into thixotropic special Al2O3 molten material slurry, using four correction center distance and automatic extrusion, the slurry evenly deposited in the foam, after 1320 ℃ Drying and solidification.

    Ceramic Foam Filter Suppliers

    AdTech Using three-dimensional network structure and connected pores organic foam as a carrier and immerse into thixotropic special Al2O3 molten material slurry, using four correction center distance and automatic extrusion, the slurry evenly deposited in the foam, after 1320 ℃ Drying and solidification.

    Product Description

    1. 3D reticulate structure
    2. High mechanical strength, no-dregs off when flapping
    3. High porosity
    4. Large surface areas, strong absorptivity of impurities
    5. Excellent thermal shock resistance
    6. Rapid improvement in filed

    Application

    Filter-PAl ceramic foam filter can effectively remove and absorb large or small impurities in molten aluminum, improve the surface quality, product performance and microstructure effectiveness. Mainly used in the domestic, construction, electricity, condensing tubes, cable and other aluminum alloy precision casting.

    Performance

    Filter-PAl ceramic foam filter can effectively remove and absorb large or small impurities in molten aluminum, improve the surface quality, product performance and microstructure effectiveness. Mainly used in the domestic, construction,
    electricity, condensing tubes, cable and other aluminum alloy precision casting.

    Ceramic Foam Filter Manufacturing Process

    Product Feature

    1. Aluminum alloy bar choose: 10-30ppi
    2. Long-term casting choose: 30-50ppi
    3. High quality aluminum profile or plate choose :40 or 50ppi
    4. Double zero wave continuous casting and rolling choose: >50ppi
    5. Other specifications can be customized as your requirments

    Product Parameter

    Specifications Aluminum?flow?range Filtration?Flow Aperture
    ?mm(inch) ?(?kg/min) ?( Ton?) (ppi)
    178×178×50mm ? ?7(inch) 25-50 3 ?10-50ppi
    254×254×50mm ? ?10(inch) 45-100 7 ?10-50ppi
    305×305×50mm ??12(inch) 90-170 15 ?10-50ppi
    381×381×50mm ??15(inch) 147-280 20 ?10-50ppi
    432×432×50mm ??17(inch) 193-367 25 ?10-50ppi
    508×508×50mm ? ??20(inch) 274-521 30 ?10-50ppi
    584×584×50mm ? ??23(inch) 369-700 35 ?10-50ppi

    Technical parameters

    Index Density
    (g. cm3)
    Rupture modulus
    (816℃ Mpa)
    Compressive
    strength(Mpa)
    Operating temperature(MAX)
    (℃)
    Item 0.52 4.8 0.51 1280
    Pore size
    Type(ppi) 10 20 30 40 50
    Pore 8- 12 18- 22 28- 32 38-42 48- 52
    average size(um) 2000 840 590 420 297
    Data of application
    Product
    Specifications(mm)
    Effective
    Filtration area(%)
    Filtration flow
    Range(kg/min)
    7in(178*178*50) 68 22-42
    9in(229*229*50) 70 42-68
    12in(305*305*50) 73 60-135
    15in(381*381*50) 79 90-240
    17in(432*432*50) 80 125- 310
    20in(508*508*50) 82 170-420
    23in(584*584*50) 84 230-580

    Usage

    1. Clean the aluminum filter box, keep it clean and intact.
    2. Put the ceramic foam filter into filter box carefully , press Sealing gasket around , avoid molten aluminum Dispersing or floating away.
    3. Use electric or gas to Preheat filter box and ceramic foam filter evenly 15-30min, make the temperature next to the molten aluminum, ceramic foam filter preheating temperature should surpass 460℃.expansion cotton will seal after heating, it makes ceramic foam filter steady in molten aluminum. preheating makes ceramic foam filter pores open and avoid occlusion expansion and contraction.
    4. Observe change of molten aluminum pressure, control the flowing molten aluminum needed, normal start pressure: 100-150mm. the pressure falls down bellow 75-100mm when molten aluminum flowing, it will grow later.
    5. Do not shock and beat ceramic foam filter in filtration. Control molten aluminum flow rate in launder.
    6. Take out ceramic foam filter and clean filter box after filtration.

    Storage: stored in ventilated and dry environment.
    Package: 5 pieces/ carton, 60 pieces/pallet.